Why use a flux?

A molten brazing filler metal will only wet and flow over a parent metal if both are substantially free of surface oxide. Simply removing surface oxide before brazing is not effective, since a new oxide layer is rapidly formed on heating. To achieve an oxide free surface, it is necessary either to:

1. Remove oxide as it is formed by the use of a suitable brazing flux.
2. Prevent oxidation during brazing by heating in a protective atmosphere or vacuum.
3. Use a self-fluxing brazing alloy - only applicable when brazing copper to copper.

Brazing fluxes are only designed to remove oxide films. Where other contaminants such as oil, paint and lacquer are present these should be removed before brazing, using either mechanical or chemical methods.

How to use a brazing flux

It is recommended that flux should be applied as a paste to the parts to be joined.

Powders can be made into pastes by stirring in water until the mixture has the consistency of thick cream. A few drops of liquid detergent added to the mixture will often improve the wetting of flux onto clean parent metals.

The flux should be applied to both joint surfaces before assembly. Application of flux after assembly places great demands on the fluidity of the molten flux and its ability to penetrate capillary joints. Flux may be applied in the following ways:

1. Brushing is an effective method of applying a thin film of paste to the joint itself and to surrounding component surfaces.
2. Brazing flux may be applied by dipping one or more components of an assembly into a container of flux. This is most effective with a paste of a thin consistency.
3. Automatic application of flux is possible and can be used for mass production; contact us for more information.
4. Hot rodding is a technique in which a warm brazing rod is dipped into flux powder and the flux adhering to the rod is transferred to the joint area. This is an effective fluxing method but difficult to achieve good penetration of capillary joints. A refinement on this technique is the use of flux coated brazing rods.

Factors which affect how a flux works

The ability of any flux to perform satisfactorily during a brazing operation will depend on the brazing temperature and time, the parent metals, and the volume of flux applied.

Temperature

To be effective the flux must be both molten and active before the brazing alloy melts, and it must remain active until the brazing alloy flows through the joint and solidifies on cooling. It is good practice to select a flux which is active at least 50oC below the solidus of the brazing alloy and which is still active at a temperature at least 50掳C above the liquidus of the brazing alloy. This will ensure that the flux is effective during the brazing operation.

Time

The flux should remove the oxides on the component and must continue to remove fresh oxide until the completion of the brazing cycle. There is a limit to the amount of oxide that the flux can dissolve, although the longer the heating cycle the more likely it is that the flux will become exhausted.

With long heating cycles the use of flux with a higher working range would be recommended. For short rapid heating cycles, it may be possible to use a flux above its recommended maximum working temperature.

Parent metals

Our fluxes are suitable for use on copper, brass, mild steel and most other common engineering materials. Special purpose fluxes exist for aluminium bronze, stainless steel, tungsten, molybdenum and tungsten carbide. Silver brazing fluxes are not effective on aluminium, magnesium, titanium or their alloys.

1. When joining copper to copper no flux is required. Heat the inserted component first then heat evenly.
   
   
2. Transfer the flame to heat all around the base of the socket.
   
   
3. When the components are a dull cherry red colour touch the rod onto the joint.
   
   
4. Use the heat from the torch to pull the filler metal into and around the joint. Cool in air after brazing.

How to use a flux coated rod

Flux coated rods combine flux and brazing filler metal in a single convenient form. They are suitable for use on joints where there is a limited gap for the filler metal.

1. As the joint is heated the flux coated rod should be touched or wiped onto the joint area. This will apply some flux and protect the component from oxidation as the joint approaches brazing temperature.
   
   
2. At brazing temperature, the now bare end of the rod should again be touched onto the joint and held in position if the alloy begins to flow.
   
   
3. Turning the rod between the fingers will ensure that the flux melts off the rod and onto the component evenly.
   
   
4. Avoid heating the rod directly with the torch flame as this will melt the flux off the rod leaving no flux available for the next joint.
   
   
5. Heat evenly to brazing temperature. Feed the bare end of the flux coated rod into the joint whilst heating the component evenly.
   
   
6. Flux residues must be completely removed by soaking in warm water for about 30 minutes.

The use of paste requires different techniques and general practices to those employed for other forms of brazing or soldering consumables. The basic principles always apply.

Location of paste deposits

Whilst no particular joint design is excluded from brazing or soldering with paste, the suitability of a component is dependent on there being a place to deposit the required amount of paste. Ideally the component should have a shoulder or ledge on which the paste can be adequately supported.

Components should be assembled and the paste applied as near to the mouth of the joint as possible. Avoid placing paste inside the joint as it may not burn off completely, restricting the flow of the flux and alloy.

If the component does not have a convenient shoulder or ledge then the paste should be applied above the joint. Any movement of the paste during heating can be controlled to direct the flux and alloy flow towards the mouth of the joint. In this case a flux binder system with minimal slump characteristics is recommended.

Dispensing of paste onto components

A major advantage of using a paste is that it can be dispensed in accurate and controlled volumes, ensuring that a particular joint receives the same amount of paste on each application.

Paste is often supplied in cartridges, which can be fitted to accurate air operated dispensing machines. Where larger volumes of paste are required a reservoir connected to a paste gun can be used. Paste can be supplied in hand cartridges for manual dispensing although this reduces the close control over paste volumes achieved with even the most basic dispenser.

Contact us about the most suitable method for dispensing paste onto a particular component; we can then formulate the paste accordingly.

The size and shape of paste deposits

The shape and design of the component govern the size and placement of the paste deposit. It is often possible to calculate an approximate amount of paste required per joint. However, in most cases a simple production test will quickly establish the correct amount to use.

Automatic dispensing

If possible, paste should be applied as a single deposit. This method needs the minimum of dispensing equipment and the least time spent on the dispensing operation.

On long joints, it may be necessary to apply more than one paste deposit. This increases the area covered by flux and alloy and is advisable particularly if the alloy is not free flowing.

Paste can be applied as a number of dots, or as a continuous stripe. In applications such as this, movement of either the dispensing nozzle or the component itself may be required during paste application.

Heating methods for brazing and soldering paste

Our paste products can be used successfully with most of the standard heating methods.

1. Fixed burners 鈥� accurate and reproducible heat patterns can be set electronically using a range of fuels. They may be arranged as single or double burners on basic shuttle or rotary indexing machines.
2. Furnace heating - uses a reducing atmosphere or vacuum to prevent or break up surface oxides during the brazing process.
3. Induction heating - quick and easily controlled heating well suited to paste products.
4. Resistance heating 鈥� works well with brazing and soldering pastes. Resistance heating with a separate filler metal and flux can cause problems because the flux acts as an insulator. Using paste will help to overcome this as the finely divided powder offers a conductive path through the flux.
5. Hand torch - pastes should be heated indirectly to ensure the paste deposit reaches the correct temperature at the same rate as the rest of the component. If heated directly, the flux in the paste will not have sufficient time to clean the parent metals and the molten filler metal alloy will not wet out onto the joint area.

Heating brazing paste

The behaviour and flow characteristics of a brazing paste when heated will depend upon its formulation, whether it contains flux and the heating method being used. A typical fluxed paste for brazing in air with a silver brazing filler metal based around the 'B1' binder system will go through the following stages:

1. On initial heating, the paste deposit will increase in size. During this early stage of heating the paste deposit should be heated slowly and indirectly to cause it to 'set'. Heating it too rapidly or directly can cause it to 'explode' or spit.
2. With further heating, the paste will either start to smoke, or if a flame is present ignite. Where ignition of the paste does not occur, for example when using RF induction or resistance heating, local exhaust ventilation should be used to remove the fume from the working environment.
3. As the heating continues the paste's appearance will change from a shiny, glossy deposit, to a dull, dry one. The binder has now been lost from the paste which has become 'set'. Once 'set' it is stable and can be subjected to a more rapid rate of heating.
4. Next the flux starts to melt, 'wetting' the parent metals and reducing surface oxides on them. Initially this takes place locally around the base of the paste deposit. As the temperature continues to increase the flux becomes more fluid, spreading out and flowing into the capillary gap present within the joint.
5. Finally, as more heat is applied the filler metal will begin to melt and then flow completely. The rate of heating at this stage needs to be sufficient to prevent liquidation of the filler metal. This is where the filler metal only partially melts leaving behind a skull of solid material and resulting in a joint that is only partially filled.
   
   

Both the binder and the flux in a paste can be changed or modified to match the needs of a particular brazing job. For example, binder systems can be supplied that collapse and spread onto a component where paste is needed over a large area.

Removal of brazing paste residues after heating

The flux residues of brazing pastes are corrosive and therefore their removal after brazing is essential. They are similar to those generated in other brazing operations and may be removed by the same methods - soaking in hot water (> 40oC for 30 minutes), soaking in 10% sulphuric acid or by mechanical removal (e.g. grit blasting). The method should depend on the type of flux present. Brazing pastes often leave a 'footprint' or mark on the component that is difficult to remove after brazing. For advice on the best method of removing the flux residues please contact us.

Heating soldering paste

Solder pastes are formulated around totally different binder systems and flux types to those used for brazing and they therefore react completely differently when heated.

Solder paste when heated initially will exhibit some slump depending upon its formulation. With further heating the deposit may bubble and heave (foam) and begin to smoke. Local exhaust ventilation should be used to remove the fumes. If heated too rapidly the paste deposit can boil and spit. Gentle, indirect heating (such as hot air heating) is recommended throughout the soldering process.

The solder paste becomes more fluid as the temperature is increased but it should remain colourless throughout the soldering operation. If the flux starts to go brown it is an indication that either it is beginning to become exhausted or that the paste has been overheated.

As the solder alloy within the paste begins to melt, the flux is displaced from the joint and floats on top of the molten solder. Fluxes and solders will always flow to the hottest point of a joint and further flow of the solder into, along or around the joint can be encouraged by creating a thermal gradient across it.

If the solder fails to wet and flow as required or forms a molten 'ball' then this is an indication that the flux has not been able to remove the oxides present on the surface of the parent materials.

This could be due to exposing the paste deposit to too high a temperature or exhausting the flux before the filler metal becomes molten. Alternatively, an inappropriate fluxed binder system was selected for the application.

Removal of soldering paste residues after heating

Flux residues from soldering paste are classified as non-corrosive, intermediate or corrosive. Non-corrosive residues may be left on the completed joint. Intermediate or corrosive flux residues should be fully removed. Warm water, mildly alkaline solution, or in the case of rosin based flux residues an organic solvent, should be used. For advice on the best method of removing the flux residues please contact us.

Storing and shelf life

Brazing and soft soldering pastes have limited shelf life and strict stock rotation should be exercised during their storage. The binder system and the filler metal powder can separate and the paste may dry out during storage. Separation or drying out of a paste is more likely if the product is not stored correctly.

Storage temperature

Braze and soft solder pastes should not be stored below 5掳C or above 25掳C. The ideal storage temperature for pastes is between 10 and 15掳C. The viscosity of brazing and soft solder pastes is affected by temperature. They are designed for use between 18 and 24掳C (Viscosity measurements are taken during production at 20掳C). If subjected to temperatures below 15掳C the paste viscosity will increase making dispensing more difficult. If stored at temperatures above 25掳C the paste will become very fluid and may separate and dry out. It is therefore recommended that pastes should be withdrawn from the storage facility some time before use and placed in the workshop environment to obtain a normal working temperature. Storing at temperatures below 5掳C can result in damaging the products irreparably.

Storage conditions

• Paste should ideally be stored in cool dry conditions away from direct sunlight and other sources of heat.
• Pastes supplied in buckets or pots should be stored in closed containers and stood with the lid upper most.
• Pastes supplied in machine cartridges or hand syringes should be stored standing up in racks with the 'follower plug' upper most and the nozzle facing down. Storing cartridges / syringes on their side can result in separation of the paste.